Res. Agr. Eng., 2012, 58(3):83-91 | DOI: 10.17221/27/2011-RAE

Degradation medium of agrocomplex - adhesive bonded joints interaction

M. Müller, P. Valášek
Department of Material Science and Manufacturing Technology, Faculty of Engineering, Czech University of Life Sciences Prague, Prague, Czech Republic

Research of degradation medium occurring in agrocomplex at the current interaction with bonded joints strength and lifetime is desired owing to the possibilities of bonding applications in this dynamically developing field. The bonding technology is used in construction of machines, lines and devices of agriculture, forestry and food industry. Among the perspectives of bonding technologies the adhesive bonding can be considered thanks to its predominant pluses. At the bonding technology or more precisely adhesive bonding technology application the limits must be characterized, which occur in the process of application in the concrete medium. On the basis of characteristics and analyses the countermeasures eliminating the negative factors can be taken. Published results set themselves the goal to know degradation processes taking place in bonded joints contemporarily with taking account of adhesive/adherend interaction with accent on application in agriculture. Experimentally found results confirm the presumption of a significant portion of the adhesive layer on the adhesive bond strength decrease in the practice due to the degradation processes.

Keywords: liquid contaminants; bonding method; cyclic degradation; bond strength; bond lifetime

Published: September 30, 2012  Show citation

ACS AIP APA ASA Harvard Chicago Chicago Notes IEEE ISO690 MLA NLM Turabian Vancouver
Müller M, Valášek P. Degradation medium of agrocomplex - adhesive bonded joints interaction. Res. Agr. Eng. 2012;58(3):83-91. doi: 10.17221/27/2011-RAE.
Share...
Download citation
  • BibTeX (.bib)
  • Bookends (.ris)
  • EasyBib (.ris)
  • EndNote (.enw)
  • EndNote 8 (.xml)
  • ISI WoS (.isi)
  • Medlars (.medlars)
  • Mendeley (.ris)
  • MODS (.xml)
  • Papers (.ris)
  • RefWorks (.txt)
  • RefManager (.ris)
  • RIS (.ris)
  • MS Word (.xml)
  • Zotero (.ris)
    • Open full article

    References

    1. Aglan H., Rowell T., Ahmed T., Thomas R., 1999. Durability assessment of composite repairs bonded to aircraft structures. Journal Adhesion Science Technology, 1: 127-148. Go to original source...
    2. Armstrong K.B., 1997. Long-term durability in water of aluminium alloy adhesive joints bonded with epoxy adhesives. International Journal of Adhesion & Adhesives, 17: 89-105. Go to original source...
    3. Brožek M., Müller M., 2004. Mechanické vlastnosti spojů lepených sekundovými lepidly (Mechanical properties of adhesive bonds glued by cyanoacrylate adhesive). Strojírenská technologie, 1: 9-15.
    4. Cererit, 2001. Bezpečnostní list pro Cererit (Safety data sheet for Cererit). Available at http://mercata.cz/pdf/bl/Cererit.pdf
    5. Colak A., Cosgun T., Bakirci A.E., 2009. Effects of environmental factors on the adhesion and durability characteristics of epoxy-bonded concrete prisms. Construction and Building Materials, 23: 758-767 Go to original source...
    6. Court R.S., Sutcliffe M.P.F., Tavakoli S.M., 2001. Ageing of adhesively bonded joints - fracture and failure analysis using video imaging techniques. International Journal of Adhesion & Adhesives, 21: 455-463. Go to original source...
    7. Crocombe A.D., 1997. Durability modelling concepts and tools for the cohesive environmental degradation of bonded structures. International Journal of Adhesion & Adhesives, 17: 229-238. Go to original source...
    8. ČSN EN 1465, 2009. Lepidla - Stanovení pevnosti ve smyku při tahovém namáhání přeplátovaných lepených sestav (Adhesives - Determination of tensile lap-shear strength of bonded assemblies).
    9. ČSN ISO 10365, 1995. Lepidla - Označení hlavních typů porušení lepeného spoje (Adhesives - Designation of main failure patterns).
    10. ČSN EN ISO 527-1, 1997. Plasty - Stanovení tahových vlastností - Část 1: Základní principy (Plastics - Determination of tensile properties - Part 1: General principles).
    11. ČSN EN ISO 3167, 2004. Plasty - Víceúčelová zkušební tělesa (Plastics - Multipurpose test specimens).
    12. ČSN EN ISO 9142, 2004. Lepidla - Směrnice k výběru laboratorních podmínek stárnutí pro hodnocení lepených spojů (Adhesives - Guide to the selection of standard laboratory ageing conditions for testing bonded joints).
    13. ČSN EN ISO 868, 2003. Plasty a ebonit - Stanovení tvrdosti vtlačováním hrotu tvrdoměru (tvrdost Shore) [Plastics and ebonite - Determination of the indentation hardness by means of a durometer (Shore hardness)].
    14. Davis M., Bond D., 1999. Principles and practices of adhesive bonded structural joints and repairs. International Journal of Adhesion & Adhesives, 19: 91-105. Go to original source...
    15. Ducháček V., 2006. Polymery - výroba, vlastnosti, zpracování, použití (Polymers - Production, Properties, Processing, Uusing). Prague, Kanag Tisk: 278.
    16. Gerald D., Pethrick R.A., 2009. Environmental effects on the ageing of epoxy adhesive joints. International Journal of Adhesion & Adhesives, 29: 77-90. Go to original source...
    17. Gledhill R.A., Kinloch A.J., 1974. Environmental failure of structural adhesive joints. Journal of Adhesion, 4: 315-333. Go to original source...
    18. Herák D., Müller M., Káranský J., Dajbych O., 2008. Bearing capacity of the bonded metal joints in the conditions of Indonesia, North Sumatra province. In: EngOpt2008 - International Conference on Engineering Optimization, June 1-5, 2008. Rio de Janeiro: 5.
    19. Kinloch A.J., 1987. Adhesion and Adhesives - Science and Technology. 1st Ed. London, Chapman and Hall: 425. Go to original source...
    20. Kinloch A.J., Osiyemi S.O., 1993. Predicting the fatigue life of adhesively-bonded joints. Journal of Adhesion, 43: 79-90. Go to original source...
    21. Kinloch A.J., Little M.S.G., Watts J.F., 2000. The role of the interphase in the environmental failure of adhesive joints. Acta Materialia, 48: 4543-4553. Go to original source...
    22. Messler R.W., 2004. Joining of Materials and Structures from Pragmatic Process to Enabling Technology. Burlington, Elsevier: 790.
    23. Müller M., Chotěborský R., 2007. Možnosti hodnocení tloušťky lepené vrstvy (Possibilities of adhesive layer thickness evaluation). Jemná mechanika a optika, 9: 247-249.
    24. Müller M., Herák D., 2010. Dimensioning of the bonded lap joint. Research in Agricultural Engineering, 56: 59-68. Go to original source...
    25. Müller M., Chotěborský R., Hrabě P., 2009. Degradation processes influencing bonded joints. Research in Agricultural Engineering, 55: 29-34. Go to original source...
    26. Novák P., 2002. Korozní inženýrství (Corrosive engineering). Available at http://www.vscht.cz/met/stranky/vyuka/labcv/korozni_inzenyrstvi_se/koroze/p_prumys. htm; http://www.vscht.cz/met/stranky/vyuka/labcv/korozni_inzenyrstvi_se/koroze/p_vody.htm
    27. Nolting A.E., Underhill P.R., Duquesnay D.L., 2008. Variable amplitude fatigue of bonded aluminum joints. International Journal of Fatigue, 30: 178-187. Go to original source...
    28. Rushforth M.W., Bowen P., McAlpine E., Zhou X., Thompson G.E., 2004. The effect of surface pretreatment and moisture on the fatigue performance of adhesivelybonded aluminium. Journal of Materials Processing Technology, 153-154: 359-365. Go to original source...
    29. Sargent J.P., 2005. Durability studies for aerospace applications using peel and wedge tests. International Journal of Adhesion & Adhesives, 25: 247-256. Go to original source...
    30. Sonawala S.P., Spontak R.J., 1996. Degradation kinetic of glass-reinforced polyester in chemical environments. Journal of Material Science, 31: 4757-4767. Go to original source...

    This is an open access article distributed under the terms of the Creative Commons Attribution-NonCommercial 4.0 International (CC BY NC 4.0), which permits non-comercial use, distribution, and reproduction in any medium, provided the original publication is properly cited. No use, distribution or reproduction is permitted which does not comply with these terms.


    Return to the content